Zinc spray

Art.-no. 0893113114

Prices for customers after login

Quantity

PU

Show availability in Würth trade store

Exclusively for trade customers

Register now and access more than 15,000 products

Long-term protection and repair of metallic surfaces

Excellent corrosion protection


  • The metal is actively protected, even with minor damage

  • Over 100 hours of salt-spray resistance (DIN 50021 SS)


Excellent adhesive properties on bare metal



Excellent spot welding properties

Notice

Not suitable as adhesive base for PU, MS polymer and hybrid sealing compounds.

Product information

Würth Catalogue(X)

Catalogue page as PDF 1  |  2

Datasheets(X)

Safety data sheet

Application area

For visual enhancement, repair and protection against corrosion of metallic surfaces.

Contents

400 ml

Chemical basis

Alkyd resin combination

Colour

Zinc, bright

Min. curing time

10 h

Fully hardening/curing conditions

At recommended dry layer thickness

Max. curing time

12 h

Resistance in salt-spray test

100 h

Max. temperature resistance

240 °C

Dust-drying time

15 min

Dry layer thickness (first back-and-forth motion)

30 µm

Conditions for dust-drying time

at recommended dry layer thickness

Purity rating zinc

99.995 %

Zinc content in the dry film

44.6 %

Coating thickness

70 µm

Recoatable/Can be painted over

Conditional, preliminary testing required

Grip strength conditions

at recommended dry layer thickness

Substrates with good adhesion

Ferrous metals
PMMA
Polycarbonate
Polystyrene
Zinc plated surfaces

Spot weldable

Yes

AOX-free

Yes

Cross-cut test

MAN 0-1

Min./max. grip strength

15-20 min

Cross-cut test conditions

in accordance with DIN 53151

Conditions for resistance in salt-spray test

in accordance with DIN 50021

Min./max. processing temperature

5 to 35 °C

Shelf life from production

24 Month

Conditions to maintain shelf life from production

at 10°C to 25°C

Min. flashing point

-42 °C

Suitable glove:

 
Product
Description
Chemical protective glove, Butyl
Chemical protective glove, Butyl
Description:
Permeation level: 2
Gas-tight and resistant to exhaust gases produced by combustion processes
Nitrile chemical protective glove
Nitrile chemical protective glove
Description:
Permeation level: 1
Cotton velour lining
Nitrile chemical protective glove, heavy-duty
Nitrile chemical protective glove, heavy-duty
Description:
Permeation level: 2
Long, heavy-duty design
Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.
Measured breakthrough time
Permeation level
< 10 min
0
≥ 10 min
1
≥ 30 min
2
≥ 60 min
3
≥ 120 min
4
≥ 240 min
5
≥ 480 min
6

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.
Art.-no. Cust. Mat. No.

Hazardous Material

Product information

Würth Catalogue

Catalogue page as PDF  | 

Flip catalog

Datasheets()

Datasheets ()

CAD Data  | 

Certificates/Documents

 | 

 | 

Technical information